Enhanced electric power generation in PZT ceramics via stress control

This study aimed to enhance the electric power generation of lead zirconate titanate piezoelectric (PZT) ceramics by optimizing stress distribution. Specifically, it focused on applying high stress over a broad area of the PZT ceramic to induce shape deformation in the PZT plate. Pre-straining the PZT plate into an arch shape improved voltage generation, reaching its peak at a maximum deflection of 0.04 mm due to the expanded and intensified stress distribution. However, exceeding this deflection threshold led to a decline in voltage output due to material degradation, including crack formation and 90° domain switching. Finite element analysis confirmed that the increased stress distribution in the pre-strained PZT plate contributed to higher voltage output. Additionally, electron backscatter diffraction analysis revealed that at higher pre-strains (deflection of 0.08 mm), 90°domain switching occurred, resulting in increased internal strain and potential crack formation. Experimental investigations using bulk PZT rods further demonstrated that moderate pre-straining effectively enhanced voltage output.

This version of the article has been accepted for publication, after peer review (when applicable) and is subject to Springer Nature’s AM terms of use, but is not the Version of Record and does not reflect post-acceptance improvements, or any corrections. The Version of Record is available online at: http://dx.doi.org/10.1007/s41779-025-01298-6

This fulltext file will be available in Oct. 2026.