MDPI AG Acta Medica Okayama 1999-4923 17 7 2025 Development of an Antimicrobial Coating Film for Denture Lining Materials 902 EN Kumiko Yoshihara National Institute of Advanced Industrial Science and Technology (AIST), Health and Medical Research Institute Takeru Kameyama Graduate School of Natural Science and Technology, Okayama University Noriyuki Nagaoka Dental School, Advanced Research Center for Oral and Craniofacial Science, Okayama University Yukinori Maruo Department of Prosthodontics, Okayama University Yasuhiro Yoshida Department of Biomaterials and Bioengineering, Faculty of Dental Medicine, Hokkaido University Bart Van Meerbeek BIOMAT, Department of Oral Health Sciences, KU Leuvem Takumi Okihara Graduate School of Natural Science and Technology, Okayama University Background/Objectives: Denture hygiene is essential for the prevention of oral candidiasis, a condition frequently associated with Candida albicans colonization on denture surfaces. Cetylpyridinium chloride (CPC)-loaded montmorillonite (CPC-Mont) has demonstrated antimicrobial efficacy in tissue conditioners and demonstrates potential for use in antimicrobial coatings. In this study, we aimed to develop and characterize CPC-Mont-containing coating films for dentures, focusing on their physicochemical behaviors and antifungal efficacies. Methods: CPC was intercalated into sodium-type montmorillonite to prepare CPC-Mont; thereafter, films containing CPC-Mont were fabricated using emulsions of different polymer types (nonionic, cationic, and anionic). CPC loading, release, and recharging behaviors were assessed at various temperatures, and activation energies were calculated using Arrhenius plots. Antimicrobial efficacy against Candida albicans was evaluated for each film using standard microbial assays. Results: X-ray diffraction analysis confirmed the expansion of montmorillonite interlayer spacing by approximately 3 nm upon CPC loading. CPC-Mont showed temperature-dependent release and recharging behavior, with higher temperatures enhancing its performance. The activation energy for CPC release was 38 kJ/mol, while that for recharging was 26 kJ/mol. Nonionic emulsions supported uniform CPC-Mont dispersion and successful film formation, while cationic and anionic emulsions did not. CPC-Mont-containing coatings maintained antimicrobial activity against Candida albicans on dentures. Conclusions: CPC-Mont can be effectively incorporated into nonionic emulsion-based films to create antimicrobial coatings for denture applications. The films exhibited temperature-responsive, reversible CPC release and recharging behaviors, while maintaining antifungal efficacy, findings which suggest the potential utility of CPC-Mont-containing films as a practical strategy to prevent denture-related candidiasis. No potential conflict of interest relevant to this article was reported.