Kanadani, Teruto Faculty of Engineering Okayama University of Science
The relationship between occurrence of serration and reversion heat treatment was studied by tensile test on Al-10mass%Zn alloy. Serration was observed for the furnace cooled specimen, but not for the as-quenched one and the shortly aged one, which result is difficult to be interpreted by the Cottrell theory. The stress amplitude in the serration increased with increasing the time of annealing for reversion up to 10ks and then stayed at a constant value which might be interpreted by the Cottrell theory. The stress amplitude in the serration decreased with increasing the annealing temperature, which is contrary to the prediction by the Cottrell theory. The specimen directly annealed without aging and the one annealed after aging agreed well with each other in the tensile strength and the stress amplitude in the serration, which suggests solute clusters as the cause of serration.
Memoirs of the Faculty of Engineering, Okayama University
Faculty of Engineering, Okayama University
|Eprints Journal Name||