A Ba-Ti composite oxide was formed on a NOx storage and reduction catalyst via impregnation of a Ba-Ti precursor solution composed of H(2)O(2) added to a complex prepared using the citric acid method. The structure of the Ba-Ti composite in solution was analyzed by chemical composition analysis and FT-Raman and UV-vis spectroscopy. MM2 calculations were performed to propose its chemical structure. Both Ba and Ti together were found to form a composite molecule in the solution. Furthermore, TEM-EDX and XRD analyses of the Ba-Ti composite oxide on the catalyst prepared by impregnation with the Ba-Ti composite aqueous solution revealed that Ba and Ti in the catalyst were highly dispersed at the nm scale. The formation of the Ba-Ti composite oxide on the NSR catalyst enhanced sulfur desorption efficiency and led to high-performance NO(X) conversion as a NO(X) storage and reduction activity catalyst after desulfation treatment. It was assumed that the existence of nano-scaled Ba compounds combined with Ti was efficient for the inhibition of the sintering of barium sulfate and its facile decomposition. It was found that dispersion of Ba compounds for NO(X) storage materials using a Ba-Ti complex solution is an efficient way to improve the durability of NSR catalysts.
Applied Catalysis B: Environmental
Elsevier Science BV.
© 2011 Elsevier B.V. All rights reserved.
|Web of Sience KeyUT|