Effects of ultrasonic treatment on the preparation of transparent glass-ceramic phosphor
FullText URL
Author
Inoue, Teruhide
Nakashima, Mizuho
Miura, Yoshinari
Abstract
The effects of ultrasonic surface treatment (UST) on the crystallization behavior and optical emission properties were investigated for the transparent glass-ceramics prepared from calcium aluminosilicate glasses co-doped with Eu(2+), Nd(3+). The glass-ceramics A were prepared by sintering a glass 45CaO・45Al(2)O(3)・10SiO(2) (mol%) containing 0.5Eu(2)O(3)+1Nd(2)O(3) under a 2% H(2)+98% Ar reducing atmosphere. In the glass-ceramics A, three crystalline phases, CaAl(2)O(4) (CA), CaAl(4)O(7) (CA2) and Ca(2)Al(2)SiO(7) (CAS) were commonly confirmed by X-ray diffraction. No drastic change in the amount of the precipitated crystalline phases was observed even in the case using UST of CA powders. It was suggested that the optical emission properties of the glass-ceramics A was responsible for the CA2 crystals. The glass-ceramics B were also prepared from a 51CaO・42Al(2)O(3)・7SiO(2) glass. The CA crystals were separately precipitated in the glass-ceramics B. In particular, a large amount of CA was successfully produced by stirring the UST suspension to prevent the sedimentation of the UST particles. The glass-ceramic B so-prepared showed strong photoluminescence but weak phosphorescence compared with other glass-ceramics B, indicating that the photoluminescence and phosphorescence were originated in different electron-trapping levels. The amount of the trap levels associated with the long lasting phosphorescence, such as oxygen vacancies, was probably small in the glass-ceramic B prepared with the stirring UST.
Keywords
ultrasonic surface treatment (UST)
surface crystallization
glass-ceramics
long lasting phosphorescence
calcium aluminosilicate glass
Publication Title
岡山大学環境理工学部研究報告
Published Date
2002-03-22
Volume
volume7
Issue
issue1
Publisher
岡山大学環境理工学部
Publisher Alternative
Faculty of Environmental Science and Technology, Okayama University
Start Page
113
End Page
118
ISSN
1341-9099
NCID
AN10529213
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
日本語
File Version
publisher
NAID
Eprints Journal Name
fest