Morphology Control of Aromatic Polymers during Polymerization
FullText URL
Author
Yamashita, Yuhiko
Tsugita, Hiroshi
Yokoyama, Fumiyoshi
Abstract
Morphology and formation mechanism of poly (4'-oxy-4-biphenylcarbonyl) (POBP) crystals obtained by solution polymerization were firstly treated. It was concluded that the formation mechanism of the bundlelike aggregates of fibrillar crystals in POBP was fundamentally simillar to that in POB whiskers. Secondly the copolymerization effects of m-acetoxybenzoic acid and 4-(4-acetoxyphenyl) benzoic acid on the morphology of POB whiskers were studied. The experimental results strongly supported our proposal for the formation mechanism of whiskers which was consisted of crystallization of oligomers with a critical length as lamellae from solution and solid state polymerizationof oligomers between lamellae. Finally, the formation mechanism of poly (p-oxycinnamoyl) spherical products during solution polymerization was treated. The formation of these spherical products could be understood by overlapped phase diagram of melting depression curve and consolute curve of oligomers-solvent system.
Keywords
morphology control
aromatic polymers
phase separation
polymer whisker
polymer beads
rigid rod polymers
Publication Title
岡山大学環境理工学部研究報告
Published Date
1996-03
Volume
volume1
Issue
issue1
Publisher
岡山大学環境理工学部
Publisher Alternative
Faculty of Environmental Science and Technology, Okayama University
Start Page
221
End Page
227
ISSN
1341-9099
NCID
AN10529213
Content Type
Departmental Bulletin Paper
OAI-PMH Set
岡山大学
language
日本語
File Version
publisher
NAID
Eprints Journal Name
fest